About cookies on this site Our websites require some cookies to function properly (required). In addition, other cookies may be used with your consent to analyze site usage, improve the user experience and for advertising. For more information, please review your options. By visiting our website, you agree to our processing of information as described in IBM’sprivacy statement. To provide a smooth navigation, your cookie preferences will be shared across the IBM web domains listed here.
Publication
Applied Physics Letters
Paper
Magnetic imaging of ion-irradiation patterned Co/Pt multilayers using complementary electron and photon probes
Abstract
The three-dimensional magnetic structure and reversal mechanism of patterned Co/Pt multilayers, were imaged using complementary Lorentz transmission electron microscopy (in-plane component) and magnetic transmission x-ray microscopy (perpendicular magnetization). The Co/Pt films with perpendicular anisotropy were patterned by ion irradiation through a stencil mask to produce in-plane magnetization in the irradiated regions. The boundaries of the patterns, defined by the transition from out-of-plane to in-plane magnetization, were found to be determined by the stencil mask. The nucleation fields were substantially reduced to 50 Oe for the in-plane regions and 1 kOe for the perpendicular regions, comparing to 4.5 kOe for the as-grown film. The perpendicular reversals were found to always originate at the pattern boundaries. © 2001 American Institute of Physics.