About cookies on this site Our websites require some cookies to function properly (required). In addition, other cookies may be used with your consent to analyze site usage, improve the user experience and for advertising. For more information, please review your options. By visiting our website, you agree to our processing of information as described in IBM’sprivacy statement. To provide a smooth navigation, your cookie preferences will be shared across the IBM web domains listed here.
Publication
MRS Proceedings 2003
Conference paper
Crystallinity and wet etch behavior of HfO2 films grown by MOCVD
Abstract
The crystallinity and wet etching behaviors of ultrathin (<10 nm) HfO2 films grown by metal organic chemical vapor deposition (MOCVD) were examined as a function of deposition temperature, film thickness, and post-deposition annealing. Films 3 nm in thickness deposited at 400 or 500°C were amorphous as-deposited and slowly etchable in aqueous HF; after annealing at 700°C, the same films showed some nanocrystallinity and were impervious to HF. However, thicker films grown under the same conditions showed significant crystallinity and were impervious to HF even as-deposited. These observations, in combination with measurements on various samples etched back by an Ar + ion damage/wet etch process, suggest a film structure comprising an initially amorphous near-interface region capped with a HF-resistant crystalline upper layer. It was found that the initially amorphous near-interface region (the bottom 1-3 nm) of films grown at 500°C can be induced to at least partially crystallize as the upper part of the film starts becoming crystalline as-deposited, but that this near-interface region remains at least partially amorphous after annealing at 700°C.