About cookies on this site Our websites require some cookies to function properly (required). In addition, other cookies may be used with your consent to analyze site usage, improve the user experience and for advertising. For more information, please review your options. By visiting our website, you agree to our processing of information as described in IBM’sprivacy statement. To provide a smooth navigation, your cookie preferences will be shared across the IBM web domains listed here.
Publication
Applied Physics Letters
Paper
Investigation of the silicon beading phenomena during zone-melting recrystallization
Abstract
During recrystallization of encapsulated silicon films on SiO2, by the graphite strip heater technique, the silicon sometimes breaks apart and agglomerates into small beads or stripes. By secondary ion mass spectroscopy analysis, it was found that a high concentration of nitrogen at the interface between the silicon and the top SiO2 capping layer is needed to prevent this from occurring. Incorporation of hydrogen into the crystallization ambient was found to cause the beading to occur. The initial stages of the bead formation were investigated by scanning electron cross-section microscopy.