About cookies on this site Our websites require some cookies to function properly (required). In addition, other cookies may be used with your consent to analyze site usage, improve the user experience and for advertising. For more information, please review your options. By visiting our website, you agree to our processing of information as described in IBM’sprivacy statement. To provide a smooth navigation, your cookie preferences will be shared across the IBM web domains listed here.
Publication
IITC 2007
Conference paper
Impact of Cu microstructure on electromigration reliability
Abstract
The effect of Cu microstructure on electromigration (EM) has been investigated. A variation in the Cu grain size distributions between wafers was achieved by adjusting the wafer annealing process step after Cu electroplating and before Cu chemical mechanical polishing. Void growth morphology was observed by in-situ and ex-situ scanning electron microscope (SEM) techniques. The Cu lifetime and mass flow in samples with bamboo, near bamboo, bamboo- polycrystalline mixture, and polycrystalline grain structures were measured. The introduction of polycrystalline Cu line grain structure in fine lines for the 65 nm node technology and beyond markedly reduced the Cu EM reliability. The smaller Cu grain size distribution resulted in a shorter EM lifetime and a faster mass flow. The EM activation energies for Cu along Cu/amorphous a-SiCxNyHz interface and grain boundary were found to be 0.95 and 0.79 eV, respectively. © 2007 IEEE.