About cookies on this site Our websites require some cookies to function properly (required). In addition, other cookies may be used with your consent to analyze site usage, improve the user experience and for advertising. For more information, please review your options. By visiting our website, you agree to our processing of information as described in IBM’sprivacy statement. To provide a smooth navigation, your cookie preferences will be shared across the IBM web domains listed here.
Publication
Journal of Applied Physics
Paper
Structure, magnetization, and thermal stability of (100) FeCu films deposited on Pd/Cu/Si(100)
Abstract
(100)-oriented FeCu films, containing 80 and 50 at. % Fe, have been deposited on (100) Si using (100) Pd/Cu seed layers. Heating of the samples helps identify the structures of the FeCu films, especially the one with 50 at. % Fe. The FeCu(50/50) film shows a structure with possibly two phases: one with a lattice spacing close to that of (100) Fe, and one to that of (100) Cu, henceforth assigned to the Fe- and Cu-stabilized FeCu phases, respectively. The FeCu(80/20) film shows only one phase, with a lattice spacing close to that of (100) Fe. Ferromagnetic characteristics are detected up to an anneal of 30 min at 600°C for the FeCu(80/20) films, with a reduced saturation magnetization above 400°C. For the FeCu(50/50) films, their ferromagnetic characteristics remain little changed up to 300°C, with reduced saturation magnetization at 400°C, and disappear completely after an anneal at 500°C. The results are compared with those containing elemental Fe layers deposited on different metal seeds, and the reaction mechanisms of the present structures are discussed.