About cookies on this site Our websites require some cookies to function properly (required). In addition, other cookies may be used with your consent to analyze site usage, improve the user experience and for advertising. For more information, please review your options. By visiting our website, you agree to our processing of information as described in IBM’sprivacy statement. To provide a smooth navigation, your cookie preferences will be shared across the IBM web domains listed here.
Publication
Journal of Materials Research
Paper
Stress gradients observed in Cu thin films induced by capping layers
Abstract
Glancing-incidence x-ray diffraction (GIXRD) has been applied to the investigation of depth-dependent stress distributions within electroplated Cu films due to overlying capping layers. Cu films, 0.65 μm thick, plated on conventional barrier and seed layers received a chemical vapor deposited (CVD) SiCxNyHz cap, an electrolessly deposited CoWP layer, or a CoWP layer followed by a SiCxNyHz cap. GIXRD and conventional x-ray diffraction measurements revealed that strain gradients were created in Cu films possessing a SiCxN yHz cap, where a greater in-plane tensile stress of approximately 180 MPa was generated near the film/cap interface as a result of constraint imposed by the SiCxNyHz layer during cooling from the cap deposition temperature. Although Cu films possessing a CoWP cap without a SiCxNyHz layer did not exhibit depth-dependent stress distributions, subsequent annealing introduced stress gradients and increased the bulk Cu stress. However, a thermal excursion to liquid-nitrogen temperatures significantly reduced tensile stresses in the Cu films. © 2010 Materials Research Society.