About cookies on this site Our websites require some cookies to function properly (required). In addition, other cookies may be used with your consent to analyze site usage, improve the user experience and for advertising. For more information, please review your options. By visiting our website, you agree to our processing of information as described in IBM’sprivacy statement. To provide a smooth navigation, your cookie preferences will be shared across the IBM web domains listed here.
Publication
Journal of Applied Physics
Review
Microstructure modifications induced by bonded hydrogen in N-rich SiNx:H films
Abstract
The effect of bonded hydrogen in the atomic microstructure of nitrogen-rich SiNx:H films is investigated using extended x-ray-absorption fine-structure spectroscopy (EXAFS). The hydrogen concentration in the examined films, as measured by elastic recoil detection analysis, takes values in the range 25-33 at. %. It is shown that hydrogen, which is mostly bonded to N, alters the film microstructure, as that is determined by the nearest-neighbor distances and coordination numbers. The measured N-Si nearest-neighbor distance is modified by the presence of N-H bonds and it is shorter than that corresponding to Si3N4 by 3%. This bond length reduction is attributed to the higher electronegativity of hydrogen than that of the replaced Si atoms. In addition, the coordination number N in the nearest-neighbor shell, consisting of Si atoms, is reduced to 2 from the expected coordination of 3 in Si3N4. Furthermore, EXAFS detects the presence of partially reacted Si (a-Si:N) phase, embedded in the SiN matrix, the concentration of which depends on the deposition conditions (rf power and gas flow ratio). The existence of the a-Si:N phase is confirmed by plane-view transmission electron microscopy measurements. © 1996 American Institute of Physics.