About cookies on this site Our websites require some cookies to function properly (required). In addition, other cookies may be used with your consent to analyze site usage, improve the user experience and for advertising. For more information, please review your options. By visiting our website, you agree to our processing of information as described in IBM’sprivacy statement. To provide a smooth navigation, your cookie preferences will be shared across the IBM web domains listed here.
Abstract
We present a procedure to fabricate extremely smooth Au films supported on thin elastomeric (PDMS) substrates. Minimum rms roughness and largest grain size are obtained using Si wafers, coated with native oxide and release layers, as templates for the growth of thermally evaporated Au films. The wafers are held at a temperature of 300 °C during deposition. The Au films, up to 200 nm thick, are then transferred onto poly(dimethylsiloxane) substrates which have been previously surface-functionalized with a (3-mercaptopropyl)trimethoxysilane adhesion layer. The resulting Au films have been found by AFM to be extremely smooth with rms-roughness 2.5-4 Å and to exhibit a crystalline morphology with flat grains > 500 nm in size. Thinner films, down to 20 nm, are grown at lower temperature and are comparably smooth, but with a loss in crystalline morphology. We compare the results of this optimized procedure with other gold films grown on mica sheets as templates and to those produced using Ti-O-Si interfacial chemistry. © 2006 American Chemical Society.