About cookies on this site Our websites require some cookies to function properly (required). In addition, other cookies may be used with your consent to analyze site usage, improve the user experience and for advertising. For more information, please review your options. By visiting our website, you agree to our processing of information as described in IBM’sprivacy statement. To provide a smooth navigation, your cookie preferences will be shared across the IBM web domains listed here.
Publication
Macromolecules
Paper
Using surface active random copolymers to control the domain orientation in diblock copolymer thin films
Abstract
The structure of thin films of a symmetric diblock copolymer, P(dS-b-MMA) (dS = perdeuterated styrene, MMA = methyl methacrylate), was investigated near preferential and nonpreferential (neutral) surfaces. Neutral surfaces were achieved at the substrate and air interfaces by localizing random copolymer, P(S-r-MMA), having a styrene fraction of 0.60, to each of these interfaces. This was performed by chemically grafting the random copolymer to the substrate and anchoring a surface active random copolymer having a perfluorinated end group to the air interface, respectively. Neutron reflectivity and small-angle neutron scattering were used to determine the orientation of the lamellar microdomains for films having various boundary conditions. Successive steps of CF4 reactive ion etching followed by field emission scanning electron microscopy were used to ascertain the orientation of the microdomains as a function of film depth. For films confined between two continuous neutral surfaces, the orientation of the lamellar microdomains is observed to be perpendicular to the film surfaces throughout the entire film thickness.