About cookies on this site Our websites require some cookies to function properly (required). In addition, other cookies may be used with your consent to analyze site usage, improve the user experience and for advertising. For more information, please review your options. By visiting our website, you agree to our processing of information as described in IBM’sprivacy statement. To provide a smooth navigation, your cookie preferences will be shared across the IBM web domains listed here.
Publication
Journal of Materials Research
Paper
Resistivity-temperature behavior of dilute Cu(Ir) and Cu(W) alloy films
Abstract
The resistivities of as-deposited Cu(4.2Ir), Cu(2.0W), and Cu(2.2W) films are 32.2, 25.4, and 28.0 μΩcm, respectively. These resistivities are significantly higher than that for pure Cu films. After annealing the Cu(4.2Ir) film at constant heating rate to 800 °C and the two Cu(W) films to 950 °C, the resistivities reduce to 28.4, 4.3, and 5.2 μΩcm, respectively. The smaller reduction in resistivity for Cu(4.2Ir) compared with that for Cu(W) is partly a consequence of solute redissolution following precipitation. The variation of resistivity with temperature for the films and the Cu-rich end of the binary phase diagrams are used to categorize the decomposition behavior of the Cu(Ir) and Cu(W). These categories were defined by K. Barmak et al., J. Appl. Phys. 87, 2204 (2000). W is placed in category III along with V, Nb, Ta, Cr, Mo, Re, Ru, Os, B, and C. Ir most suitably belongs to Category II together with Fe and Co. © 2005 Materials Research Society.