About cookies on this site Our websites require some cookies to function properly (required). In addition, other cookies may be used with your consent to analyze site usage, improve the user experience and for advertising. For more information, please review your options. By visiting our website, you agree to our processing of information as described in IBM’sprivacy statement. To provide a smooth navigation, your cookie preferences will be shared across the IBM web domains listed here.
Publication
Materials Chemistry and Physics
Review
Electromigration and reliability in submicron metallization and multilevel interconnection
Abstract
There are increasing reliability concerns of electromigration-induced and thermal stress-induced failures in submicron interconnects and in multilevel interconnection with W studs. The electromigration characteristics of Al and Al-Cu submicron lines, two-level Al-Cu lines with W studs, Al fine lines under pulsed current stressing at high frequencies, and Al and Al-Cu fine lines under temperature cycling have been systematically studied. Lifetime is affected by grain size, grain morphology and bend structure in submicron metal lines. The lifetime of W stud chains is less than a half of that of Al-Cu flat lines. The discontinuity of the supply of Cu at Al-Cu/ W interfaces accounts for most of the reduction in the electromigration resistance of W stud chains. Under pulsed current stressing at frequencies 50-200 MHz, our data indicate no drastic change in lifetime within this frequency range. However, lifetime increases with duty cycle as t50αr-2.7, which is a remarkable improvement over an average current density model. Lifetime also depends explicitly on both current-on time and current-off period. The extra thermal stress induced by temperature cycling shortens the lifetime of both Al and Al-Cu fine lines by more than an order of magnitude. Our results also show that the addition of Cu in Al fine lines improves the resistance to thermal stress-induced failures, probably by the suppression of grain boundary sliding and migration. © 1993.