About cookies on this site Our websites require some cookies to function properly (required). In addition, other cookies may be used with your consent to analyze site usage, improve the user experience and for advertising. For more information, please review your options. By visiting our website, you agree to our processing of information as described in IBM’sprivacy statement. To provide a smooth navigation, your cookie preferences will be shared across the IBM web domains listed here.
Publication
Journal of Applied Physics
Paper
X-ray photoelectron spectroscopy and Auger electron spectroscopy studies of glow discharge Si1-xCx:H films
Abstract
X-ray photoelectron spectroscopy (XPS) and Auger electron spectroscopy (AES) were used to characterize the air-exposed and sputter-cleaned surfaces of glow-discharge-produced Si1-xCx:H (x=0.05 to 0.90) films. On the air-exposed surfaces, silicon was preferentially oxidized with the enriched carbon existing as graphite or hydrocarbon. Signal intensities obtained from the surfaces sputter cleaned with 1 keV Ar+ ion beams indicated no significant preferential sputtering of C to Si for these films. The values of the carbon 1s and silicon 2p and 2s binding energies as well as the valence band spectra suggested a significant change in the local atomic configurations at x∼0.6-0.7. Based on these XPS and AES results and the reported IR absorption data, a slightly cross-linked, carbon and hydrogen substituted polysilicon and an almost fully cross-linked, silicon and hydrogen substituted polycarbon were proposed to describe the structure of films below and above x∼0.6-0.7, respectively.