About cookies on this site Our websites require some cookies to function properly (required). In addition, other cookies may be used with your consent to analyze site usage, improve the user experience and for advertising. For more information, please review your options. By visiting our website, you agree to our processing of information as described in IBM’sprivacy statement. To provide a smooth navigation, your cookie preferences will be shared across the IBM web domains listed here.
Paper
Magneto-optical behavior in Co/Pt ultrathin film multilayers
Abstract
Magneto-optical Kerr effect measurements performed on (0.3 nm Co/x Pt)15 multilayers with x=0.3-2.0 nm showed all samples to exhibit strong perpendicular magnetic anisotropy. Recent work has shown that for compositions near (0.3 nm Co/1.2 nm Pt)15, both polar Kerr rotation and ellipticity exhibit bimodal reversals in which the major hysteresis loops have two distinct field-dependent steps due to the contributions of two magnetic phases. To better understand this bimodal magnetization phenomenon, Kerr rotation and ellipticity were determined as a function of radial position from the center to the edge of this disk sample. These measurements exhibit a continuous variation from two-step (bimodal) behavior in the center to single-step (unimodal) behavior at the edge. Since these films were deposited via MBE with a heated substrate, it is believed that this phenomenon is related to thermally induced variations in interface effects such as alloying, abruptness, and morphology. © 2000 American Institute of Physics.