About cookies on this site Our websites require some cookies to function properly (required). In addition, other cookies may be used with your consent to analyze site usage, improve the user experience and for advertising. For more information, please review your options. By visiting our website, you agree to our processing of information as described in IBM’sprivacy statement. To provide a smooth navigation, your cookie preferences will be shared across the IBM web domains listed here.
Publication
Solid State Ionics
Paper
Electrochromic nickel oxide thin films deposited under different sputtering conditions
Abstract
In this work, non stoichiometric nickel oxide (NiOx) thin films were deposited by r.f. reactive sputtering of a metallic nickel target in an O2-Ar atmosphere. A systematic variation of two deposition parameters was done: the oxygen flux (φ) and the r.f. power (P). The electrochemical characterization of the films was performed in aqueous electrolyte. The spectral transmittance measurements, as well as the X-ray diffraction analysis were performed ex-situ, while monochromatic transmittance and stress measurements were performed in situ. Samples deposited at low oxygen flux (or high power) are transparent, in contrast to those deposited at high oxygen flux (or low power), which are dark brown. The films were cubic NiO, with preferred orientation in the (111) direction. Lattice parameters increase with increasing oxygen flux during deposition, but decrease with increasing power. For all samples, the ratio O/Ni was greater than 1, as determined by Rutherford back-scattering analysis. Also, an important hydrogen content was found in the films. The relationship between optical, electrochemical, mechanical, structural and morphological behaviour of the above mentioned films will be reported and discussed in this work.